BASIC RAMMING MIXES |
|
| |
|
| INDUCTORAM 'XC' INDUCTORAM 'X' |
|
| This is a magnesite based ramming mass for Medium / High frequency induction furnace melting various types of ferrous / Non ferrous metals. Processing of the Raw material is done with modern machineries to avoid any sort of contamination. Tailor made material is manufactured keeping in view the size of the crucible and type of the metal. |
|
 |
|
|
| INDUCTOPATCH |
|
| Material is to be used for the patching of worn out parts of the crucible. Cracks in the lining can also be filled with the same. |
| |
| Method to Use |
| Material is to be mixed with 5-6 % 1:1 solution of Foundry Grade Sodium Silicate and water. Homogeneous mixing is required to be done. Area to be patched should be neatly dressed off slag for better performance. |
| |
| INDUCTOCOAT |
|
| Material is to be used for giving coating to water cooled copper coil. |
| |
| Method to Use |
| Homogeneous mixing is required to be done with 6-8 % plain water inorder get material in the form of paste. It is to be applied on coil. Drying can be done by putting 500 / 1000 bulbs inside the crucible. |
| |
| CHEMISTRY |
INDUCTORAM
'XC' |
INDUCTORAM
'X' |
INDUCTOTOP |
INDUCTOPATCH |
INDUCTOCOAT |
| MgO [ % ] Min. : |
70 |
88 |
70 |
70 |
88 |
| Cr2O3 [ % ] Min. : |
8 |
- |
8 |
8 |
- |
| Grading [ mm ] : |
0 – 5 |
0 - 5 |
0 – 5 |
0 – 0.5 |
0 – 0.5 |
| Sintering Temp oC Min. : |
800 |
800 |
800 |
800 |
- |
| Application Temp oC Max. : |
1750 |
1750 |
1750 |
1750 |
- |
| Application Area : |
For Stainless Steel, Other alloy Steel Continuous / Interrupted Operation |
For Stainless Steel & Manganese Steel Continuous Operation |
For Making Top of Induction Furnace above coil level |
For Patching & Filling Cracks |
For Protective coating of induction coil |
|
|
|
|
| |